Electroless coated disks for high temperature applications and methods of making the same

ABSTRACT

A disk for a hard disk drive is provided. The disk comprises a substrate comprising aluminum, and a coating layer disposed over the substrate. The coating layer comprises an alloy of Ni, X 1  and X 2 , wherein X 1  comprises one or more elements selected from the group consisting of Ag, Au, B, Cr, Cu, Ga, In, Mn, Mo, Nb, Pb, Sb, Se, Sn, Te, W, Zn and Zr, and wherein X 2  comprises either B or P, and wherein X 1  and X 2  do not comprise the same elements.

FIELD OF THE INVENTION

The present disclosure generally concerns hard disk drives and, in particular, concerns electroless coated disks for high temperature applications and methods of making the same.

BACKGROUND OF THE INVENTION

Disks used in hard drive media frequently include an aluminum-magnesium (AIMg) substrate that is plated with a material such as nickel-phosphorous (NiP) to provide a smooth surface on which to deposit magnetic recording layers upon which data may be stored. To accommodate the growing demand for increased data storage space, future hard disk drives may utilize technologies such as EAMR (Energy Assisted Magnetic Recording), which require magnetic recording layers with high magnetic anisotropy (K_(u)). Such magnetic recording layers may include alloys that require deposition temperatures in excess of 300° C. The Ni—P coating currently used to provide smooth surfaces on which to deposit the magnetic recording layer, however, cannot withstand temperatures this hot, without dramatically increasing in surface roughness.

SUMMARY OF THE INVENTION

Various embodiments of the present invention solve the foregoing problem by providing aluminum disks with a coating layer having increased thermal stability for use with high Ku magnetic recording layers.

According to one aspect of the subject disclosure, a disk for a hard disk drive comprises a substrate comprising aluminum, and a coating layer disposed over the substrate. The coating layer comprises an alloy of Ni, X₁ and X₂, wherein X₁ comprises one or more elements selected from the group consisting of Ag, Au, B, Cr, Cu, Ga, In, Mn, Mo, Nb, Pb, Sb, Se, Sn, Te, W, Zn and Zr, and wherein X₂ comprises either B or P, and wherein X₁ and X₂ do not comprise the same elements.

According to another aspect of the subject disclosure, a method of forming a disk for a hard disk drive comprises steps of providing a substrate comprising aluminum, disposing a zincate layer over the substrate, and electroless plating a coating layer over the zincate layer. The coating layer comprises an alloy of Ni, X₁ and X₂, wherein X₁ comprises one or more elements selected from the group consisting of Ag, Au, B, Cr, Cu, Ga, In, Mn, Mo, Nb, Pb, Sb, Se, Sn, Te, W, Zn and Zr, and wherein X₂ comprises either B or P, and wherein X₁ and X₂ do not comprise the same elements.

It is to be understood that both the foregoing summary of the invention and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are included to provide further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the principles of the invention. In the drawings:

FIG. 1 illustrates a disk for use in a hard disk drive according to one aspect of the subject disclosure.

FIG. 2 is a flow chart illustrating a method of forming a disk for a hard disk drive in accordance with one aspect of the subject disclosure.

DETAILED DESCRIPTION OF THE INVENTION

In the following detailed description, numerous specific details are set forth to provide a full understanding of the present invention. It will be apparent, however, to one ordinarily skilled in the art that the present invention may be practiced without some of these specific details. In other instances, well-known structures and techniques have not been shown in detail to avoid unnecessarily obscuring the present invention.

FIG. 1 illustrates a disk 100 for use in a hard disk drive according to one aspect of the subject disclosure, including a substrate 101 comprising aluminum and a coating layer 103 disposed over the substrate. Substrate 101 may comprise, for example, an alloy of aluminum (Al) and magnesium (Mg). Coating layer 103 comprises an alloy of Ni, X₁ and X₂, where X₁ comprises one or more elements selected from the group consisting of silver (Ag), gold (Au), boron (B), chromium (Cr), copper (Cu), gallium (Ga), indium (In), manganese (Mn), molybdenum (Mo), niobium (Nb), lead (Pb), antimony (Sb), selenium (Se), tin (Sn), tellurium (Te), tungsten (W), zinc (Zn) and zirconium (Zr), and X₂ comprises either B or phosphorous (P), and where X₁ and X₂ do not comprise the same elements. In accordance with one aspect of the subject disclosure, the coating layer may be between about 1 and 20 μm in thickness.

According to one aspect of the subject disclosure, disk 100 may further comprise a zincate layer 102 disposed between substrate 101 and coating layer 103. Zincate layer 102 provides a barrier that may help to prevent aluminum substrate 101 from becoming oxidized. According to another aspect of the subject disclosure, disk 100 may further comprise a magnetic recording layer 104 disposed over coating layer 103. Magnetic recording layer 104 may comprise a material that may require a high temperature (e.g., over 300° C.) deposition process, including, for example, one or more of Fe, Pt, Sm and Co.

According to certain aspects of the subject disclosure, polished AlMg/Ni—X₁—X₂ disks enjoy increased thermal stability when compared to conventional NiP-coated AIMg disks. For example, the addition of Cu to a NiP coating alloy helped to quench the magnetism of Ni which develops in the conventional NiP coating at higher temperatures (e.g., higher than 340° C.) due to the crystallization and crystal growth of Ni. In this regard, in accordance with one aspect of the subject disclosure, X₁ may comprise Cu and another element such as, for example, an element selected from the group consisting of B, In, Mo, Sn and W. Accordingly, example, the alloy may be a quaternary alloy such as Ni—Cu—In—P (i.e., where X₁ comprises Cu and In and X₂ comprises P), Ni—Cu—Mo—P (i.e., where X₁ comprises Cu and Mo and X₂ comprises P), or Ni—Cu—B—P (i.e., where X₁ comprises Cu and B and X₂ comprises P), according to certain aspects of the subject disclosure.

In accordance with one aspect of the subject disclosure, the alloy may include between about 30 and about 70 weight percent Ni, and between about 3 and about 11 weight percent X₂. Each constituent of X₁ may represent about 1.5 weight percent up to about 42 weight percent of the alloy.

According to one aspect of the subject disclosure, the coating layer may have a roughness R_(a) of less than about 0.5 nm when measured by atomic force microscopy after polishing. Because of the improved thermal stability of the coating layer, it may maintain a roughness R_(a) of less than about 1.0 nm when measured by atomic force microscopy after being heated to about 450° C., in accordance with one aspect of the subject disclosure.

FIG. 2 is a flow chart illustrating a method of forming a disk for a hard disk drive in accordance with one aspect of the subject disclosure. The method begins with step 201, in which a substrate comprising aluminum is provided. In step 202, a zincate layer is disposed over the substrate. In accordance with one aspect of the subject disclosure, the zincate layer may be deposited in an alkaline bath in high ph conditions. Alternatively, the zincate layer may be deposited via an acid zinc immersion process.

In step 203, a coating layer is provided over the zincate layer via electroless plating. The coating layer comprises an alloy of Ni, X₁ and X₂, where X₁ comprises one or more elements selected from the group consisting of Ag, Au, B, Cr, Cu, Ga, In, Mn, Mo, Nb, Pb, Sb, Se, Sn, Te, W, Zn and Zr, X₂ comprises either B or P, and where X₁ and X₂ do not comprise the same elements. The step of electroless plating the coating layer may comprise disposing the substrate in a plating bath comprising one or more metal sources for each of Ni and X₁, a reducing agent for reducing the one or more metal sources, the reducing agent comprising X₂, one or more complexors to reduce metal precipitation, one or more stabilizers, and one or more pH adjusting additives.

The plating bath may have a pH of between about 5 and about 9, in accordance with one aspect of the subject disclosure. This range of pH may allow the implementation of each constituent of X₁ from about 1.5 weight percent up to about 42 weight percent. According to another aspect of the subject disclosure, the plating bath may be maintained at a temperature between about 160° F. and about 195° F. while the substrate is disposed in the plating bath.

In accordance with one aspect of the subject disclosure, the plating bath may have a metal turn over (MTO) of less than 6. For example, according to one aspect of the subject disclosure, the MTO of the plating bath may be maintained between about 2.0 and 4.5. Maintaining the MTO within these levels allows for an economic plating performance and consistently reproducible plating results. Over the life time of the plating bath, dialysis of the orthophosphite in the bath may be utilized to keep the orthophosphite concentration stable.

In accordance with one aspect of the subject disclosure, the one or more metal sources for Ni may comprise one or more of nickel sulfate, nickel sulfamate, nickel acetate, nickel chloride, nickel hypophosphite, and nickel fluor-borate. According to another aspect of the subject disclosure, the one or more metal sources for X₁ may comprise one or more of copper sulfate, copper iodate, copper iodide, copper chloride, indium citrate, indium sulfate, indium acetate, molybdic acid, ammonium molybdate, sodium molybdate, ammonium tungstate, sodium tungstate, and indium chloride.

The reducing agent may comprise one or more of salts of hypophosphite, nickel hypophosphite, dimethylamine borane (DMAB), diethylamine borane (DEAB), amine borane, and sodium borohydride, in accordance with one aspect of the subject disclosure. In accordance with another aspect of the subject disclosure, the one or more complexors may comprise one or more of citric acid, malic acid, lactic acid, amino acids, tartaric acid, ethylenediaminetetraacetic acid (EDTA), a carboxylic acid, and any salt thereof.

According to one aspect of the subject disclosure, the one or more stabilizers may comprise one or more cations of Bi, Cd, Cu, Hg, In, Mo, Pb, Sb and Sn, AsO⁻², MoO⁻⁴, IO₃ ⁻, NO₃ ⁻, maleic acid, itaconic acid, methylbutynol, N,N-Diethyl-2-propyne-1-amine and 2-Butyne-1,4-diol. According to another aspect of the subject disclosure, the one or more stabilizers may comprise iodine or a compound thereof. The stabilizers may help to prevent the decomposition of the bath (e.g., by preventing nucleation of nickel particles in the bath).

The one or more pH adjusting additives may comprise one or more of K₂CO₃, Na₂CO₃, KHCO₃, NaHCO₃, NaOH, KOH, NH₄OH and N(CH₂CH₃)₃, in accordance with one aspect of the subject disclosure. In accordance with another aspect of the subject disclosure, the one or more pH adjusting additives may comprise a buffer selected from the group consisting of boric acid, borax, triethanolamine, triethylene pentamine, diethylenetriamine, acetate salts, propionate salts, succinate salts, and adipate salts.

In accordance with one aspect of the subject disclosure, the plating bath may further comprise one or more dispersants, anionic surfactants, nonionic surfactants, and organosulfur compounds.

In step 204, the coating layer may be polished with a slurry comprising an abrasive in an aqueous solution, in accordance with one aspect of the subject disclosure. The abrasive may include, for example, one or more of nanodiamond, alumina, titania, zirconia, germania, silica, ceria and any mixture thereof. The pH of the slurry may be maintained between 3 and 9 during the polishing.

According to one aspect of the subject disclosure, the slurry may further comprise an oxidizing agent, a complexing agent, and one or more organic amino compounds. The oxidizing agent may include, for example, one or more peroxy compounds (e.g., hydrogen peroxide), urea, permanganates, nitrates, and iodates. The complexing agent may include, for example, one or more of citric acid, lactic acid, tartaric acid, succinic acid, malonic acid, oxalic acids, amino acids or salts thereof. The organic amino compounds may include, for example, triethanolamine or the like.

According to one aspect of the subject disclosure, the slurry may further include a corrosion inhibitor comprising benzotriazole or benzoylphenylhydroxylamine. According to another aspect of the subject disclosure, the slurry may further include a stabilizer comprising one or more of ammonium lauryl sulfate, sodium dodecyl sulfate, and sodium lauryl sulfate.

According to one experimental embodiment of the subject disclosure, AIMg disks coated with the a Ni—X₁—P coating with a thickness of about 10 μm were polished using an exemplary polishing process that included an acidic polishing step at pH of about 2 and a second polishing step at a pH of about 9. Colloidal silica and/or nano-diamond were used as the abrasive in the second polishing step. In order to avoid chemical attack, the second step polishing slurry did not contain aggressive oxidizers, such as H₂O₂. The second polish step proceeded with a very low removal rate of <0.02 μm/min and left the Ni—X₁—P surface, after a wash step using conventional surfactants, smooth and defect free (e.g., with a R_(a) measured by AFM of 0.2 nm over a 10×10 μm area). Corrosion of the Ni—X₁—P coating was not observed.

According to various experimental embodiments of the subject disclosure, polished AIMg/Ni—X₁—P (e.g., where X₁═Cu, CuMo, or CuIn) disks have proven to exhibit an increased thermal stability when compared to conventional NiP-coated AIMg disks. Temperature dependent magnetic measurements on exemplary AIMg disks coated with Ni—Cu—P showed that the addition of Cu to the coating alloy helped to quench the magnetism of Ni which develops in the conventional NiP coating at higher temperatures (e.g., higher than 340° C.) due to the crystallization and crystal growth of Ni. This was demonstrated when disks were cycled through a multi module manufacturing-type sputtering machine and heated in vacuum (at 10⁻⁷ to 10⁻⁸ Torr) to a temperature of about 450° C. The disks were held at the OD by spring-loaded stainless steel pins. The pins held the disks fixed in a paddle which was driven through the sputtering machine to subsequent deposition, heating and cooling modules. The heater station was equipped with two resistance heater coils heating each side of the disks by radiation. No additional coatings were applied to the disks for the test. Each disk's surface temperature was measured by a high temperature pyrometer, which probed the disk surface immediately after it was transferred out of the heater chamber. A heater power of about 1300 W was applied for about 10 s to increase the disk temperature to about 450° C. After heating, the disk was transferred out of the sputtering machine without passing a cooling station. None of the disks were warped, showed OD dings or other damage induced by the heat. The coatings on conventional AIMg/Ni—P disks had a hazy appearance after the test indicating a substantial increase in surface roughness (as was subsequently confirmed by AFM). Surfaces of disks with the Ni—X₁—P coating remained shiny and specular. AFM Ra measurements on those disks confirmed that the coating did not degrade at temperatures of about 450° C.

The description of the invention is provided to enable any person skilled in the art to practice the various embodiments described herein. While the present invention has been particularly described with reference to the various figures and embodiments, it should be understood that these are for illustration purposes only and should not be taken as limiting the scope of the invention.

There may be many other ways to implement the invention. Various functions and elements described herein may be partitioned differently from those shown without departing from the spirit and scope of the invention. Various modifications to these embodiments will be readily apparent to those skilled in the art, and generic principles defined herein may be applied to other embodiments. Thus, many changes and modifications may be made to the invention, by one having ordinary skill in the art, without departing from the spirit and scope of the invention.

A reference to an element in the singular is not intended to mean “one and only one” unless specifically stated, but rather “one or more.” The term “some” refers to one or more. Underlined and/or italicized headings and subheadings are used for convenience only, do not limit the invention, and are not referred to in connection with the interpretation of the description of the invention. All structural and functional equivalents to the elements of the various embodiments of the invention described throughout this disclosure that are known or later come to be known to those of ordinary skill in the art are expressly incorporated herein by reference and intended to be encompassed by the invention. Moreover, nothing disclosed herein is intended to be dedicated to the public regardless of whether such disclosure is explicitly recited in the above description. 

What is claimed is:
 1. A disk for a hard disk drive, comprising: a substrate comprising aluminum; and a coating layer disposed over the substrate, the coating layer comprising an alloy of Ni, X₁ and X₂, wherein X₁ comprises Cu and an element selected from the group consisting of B, In, Mo, and W, wherein X₂ comprises either B or P, wherein X₁ and X₂ do not comprise the same elements, and wherein the alloy comprises between about 1.5 and about 42 weight percent of each constituent of X₁ and between about 3 and about 11 weight percent X₂.
 2. The disk according to claim 1, wherein the alloy is one of Ni—Cu—In—P, Ni—Cu—Mo—P, and Ni—Cu—B—P.
 3. The disk according to claim 1, wherein the alloy is a quaternary alloy.
 4. The disk according to claim 1, wherein the alloy comprises between about 30 and about 70 weight percent Ni.
 5. The disk according to claim 1, wherein the coating layer is between about 1 and 20 μm in thickness.
 6. The disk according to claim 1, wherein the coating layer has a roughness R_(a) of less than about 0.5 nm when measured by atomic force microscopy.
 7. The disk according to claim 1, wherein the coating layer maintains a roughness R_(a) of less than about 1.0 nm when measured by atomic force microscopy after being heated to about 450° C.
 8. The disk according to claim 1, further comprising a zincate layer disposed between the substrate and the coating layer.
 9. The disk according to claim 1, wherein the substrate comprises Al—Mg.
 10. The disk according to claim 1, further comprising a magnetic recording layer disposed over the coating layer, the magnetic recording layer comprising one or more of Fe, Pt, Sm and Co.
 11. The hard disk drive comprising the disk according to claim
 1. 